| Applicable material | Material pre-processing | Composition (second floor) | Film forming conditions | Thickness | Effect simulation diagram |
| Aluminum, stainless steel (non-magnetic substrate) | Sandblasting | Primer, top coat | Primer + top coat: 280℃x10min | 35-40μ |  |
| Recommended application areas |  | ||||
| Coating parameters | Primer | Topcoat |
| Solid content % | 45±2 | 40±2 |
| Viscosity (Iwata 2# cup) | 20±2 | 20±2 |
| Coating area m²/kg | 7-8 | 10-11 |
| Coating performance parameters | Testing conditions | Result |
| Continuous applicable temperature | Open flame or induction cooker | Qualified below 300℃ |
| Gloss | Photometer | 40±2° |
| Hardness | Hardness Tester | ≥6H |
| Adhesion | White Grid Knife | 100/100 5 consecutive times |
| Abrasion resistance | 3M Scouring pad 1.5kg | ≥10000 |
| Non-sticky | No fried eggs | ≥400 |
| Corrosion resistance (salt water) | 5%NaCl boiled | No change in coating for 48 hours |